Research and development of calcium phosphate coating bioabsorption fibers
| Project/Area Number |
21791940
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Dental engineering/Regenerative dentistry
|
|---|
| Research Institution | The University of Tokushima |
|---|
Principal Investigator |
TAKANO Hideyuki The University of Tokushima, 病院, 医員 (30380091)
|
|---|
| Project Period (FY) |
2009 – 2010
|
| Keywords | インテリジェントマテリアル / 人工骨 / ハイブリッド材料 / 次世代型 |
|---|
| Research Abstract |
Calcium phosphate (a -TCP, (3-TCP) that dissolved to Fineflex that was living body absorption line and hydroxyapatite (HAP) were coated. It was a soaking experiment and ph was a neutral. What sintered at 1000℃ showed strongest strength in the forced duction test. When this coating fibre was made like the disk, and osteoclast-like cells were cultured on that, the formation of the resorption lacuna was admitted in bonding and the right under of a lot of osteoclasts.
|