2010 Fiscal Year Final Research Report
Development of new function by suppression of martensitic transition in Fe-Pt ally
Project/Area Number |
21860009
|
Research Category |
Grant-in-Aid for Research Activity Start-up
|
Allocation Type | Single-year Grants |
Research Field |
Physical properties of metals
|
Research Institution | Tohoku University |
Principal Investigator |
FUJIEDA Shun Tohoku University, 多元物質科学研究所, 助教 (60551893)
|
Project Period (FY) |
2009 – 2010
|
Keywords | ポリオール法 / ナノ粒子 / Fe-Pt合金 |
Research Abstract |
The reduction of Fe and Pt salts in the polyol solution has been examined to obtain the Fe-Pt alloy fine particles with a fcc structure. The fine particles of the Fe-Pt ally with fcc structure are obtained by the reduction of Fe and Pt salts with the molar ratio Fe/Pt=2.3 at 403 K. Their Fe concentration is about 50 at %. Similar fine particles are obtained when the Fe and Pt metal salt with the molar ratio Fe/Pt>2.3 is reduced below 403 K. These results suggest that the formation of Fe-Pt alloy fine particles with the Fe concentration of about 50 at % is enhanced by the reduction in relatively both low reaction temperature and high Fe concentration solution.
|