2021 Fiscal Year Annual Research Report
固体電解質を用いたコバルト酸ストロンチウム薄膜の電気化学プロトン化
| Project/Area Number |
21J10042
|
|---|
| Research Institution | Hokkaido University |
|---|
Principal Investigator |
楊 倩 北海道大学, 情報科学院, 特別研究員(DC2)
|
|---|
| Project Period (FY) |
2021-04-28 – 2023-03-31
|
| Keywords | Solid electrolyte / SrCoOx / Protonation / Redox reaction |
|---|
| Outline of Annual Research Achievements |
Several SrCoOx-based electrochemical devices have been proposed, but solid-state protonation from SrCoO2.5 to HxSrCoO2.5 (x = 1, 1.5, and 2) at room temperature has not been demonstrated thus far due to the absence of an appropriate solid electrolyte. I demonstrated a solid-state electrochemical protonation of SrCoO2.5 using mesoporous amorphous 12CaO・7Al2O3 (CAN) film as the solid electrolyte. The crystalline phase discretely changed from SrCoO2.5 to HSrCoO2.5, H1.5SrCoO2.5, and H2SrCoO2.5 through formation of an intermediate phase of H1.25SrCoO2.5. H1.5SrCoO2.5 was colorless transparent and showed weak ferromagnetism. The present results indicate that the CAN film can be used as the solid electrolyte for the protonation treatment of TMOs. This work has been published in ACS Appl. Electron. Mater. 3, 3296-3300 (2021). Further, I created a solid-state thermal transistor using SrCoOx and YSZ and submitted a patent.
|
| Research Progress Status |
翌年度、交付申請を辞退するため、記入しない。
|
| Strategy for Future Research Activity |
翌年度、交付申請を辞退するため、記入しない。
|