Synthesis and Characterization of Photo-degradable Crosslinked Elastomer

2023 Fiscal Year Final Research Report

• Project/Area Number: 21K04699
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26040:Structural materials and functional materials-related
• Research Institution: Teikyo University of Science & Technology
• Principal Investigator: Ishida Yoshihito 帝京科学大学, 総合教育センター, 講師 (90635137)
• Project Period (FY): 2021-04-01 – 2024-03-31
• Keywords: ゴム / 光分解 / 架橋 / マイクロプラスチック / 高分子化学

Outline of Final Research Achievements

In this study, synthesis of photodegradable urethane and acrylic rubbers by introducing a photodegradable crosslinker with a quinone methide unit. The obtained rubbers have no structural differences from conventional rubbers other than the crosslinker, and no significant differences in mechanical properties were observed due to the introduction of the photodegradable crosslinker. Since polyurethane rubber is photodegradable in the polymer main chain itself, a competitive photodegradation reaction between the cross-linking point and the main chain occurred. Therefore, by using acrylate main chain without photodegradability, it was found that the degradation of rubber based only on the degradation of the photodegradable cross-linking points proceeds.

Free Research Field

高分子化学

Academic Significance and Societal Importance of the Research Achievements

本研究で合成したキノンメチド骨格を有する架橋剤やその誘導体を用いることで、身の回りのさまざまなゴムに対して機械的性質を維持しつつ分解性を付与することができると考えられる。また、本研究で合成した架橋剤は、光分解性保護基を有するもののみであった。しかし、酸や塩基、酸化還元反応などさまざまな刺激により脱保護される保護基を導入することによって、任意の刺激により分解するゴム材料を合成することが可能であると考えられる。本研究で得られた知見は、現在身の回りで利用されているさまざまなゴムへと適用できるものであり、実際に適用されることで現在問題となっているマイクロプラスチック問題の解決に貢献できると考えられる。