Bone quality analysis of tissue surrounding implant placement by Raman spectroscopy

2023 Fiscal Year Final Research Report

• Project/Area Number: 21K09966
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 57040:Regenerative dentistry and dental engineering-related
• Research Institution: Osaka Dental University
• Principal Investigator: Okazaki Joji 大阪歯科大学, 歯学部, 名誉教授 (80169094)
• Co-Investigator(Kenkyū-buntansha): 小林 靖之 地方独立行政法人大阪産業技術研究所, 森之宮センター, 総括研究員 (00416330) ; PEZZOTTI G. 京都工芸繊維大学, 材料化学系, 教授 (70262962) ; 小正 聡 大阪歯科大学, 歯学部, 講師 (70632066)
• Project Period (FY): 2021-04-01 – 2024-03-31
• Keywords: ラマン分光法 / インプラント / 大気圧プラズマ

Outline of Final Research Achievements

Bone quality evaluation methods are essential to evaluate bone strength after implant placement. In the past, we have only evaluated the mineral components of bone when we have examined the surface analysis of material surfaces, which is insufficient to explain the bone condition. Therefore, we investigated a method to evaluate bone quality using Raman spectroscopy. We analyzed the effects of atmospheric pressure plasma treatment on the surface of pure titanium metal from the viewpoint of bone quality, and found that the amount of apatite formation was higher in the experimental group.