Study on a new processing method for low-alloy steel aiming to achieve both corrosion resistance and fatigue properties.

2023 Fiscal Year Final Research Report

• Project/Area Number: 21K14059
• Research Category: Grant-in-Aid for Early-Career Scientists
• Allocation Type: Multi-year Fund
• Review Section: Basic Section 18020:Manufacturing and production engineering-related
• Research Institution: Tokyo Metropolitan University
• Principal Investigator: IJIRI MASATAKA 東京都立大学, システムデザイン研究科, 助教 (10840374)
• Project Period (FY): 2021-04-01 – 2024-03-31
• Keywords: キャビテーション / 赤錆 / 疲労特性 / 耐食性

Outline of Final Research Achievements

Rust in rust-prone steel is promoted in water by corrosive factors. Therefore, to prevent the formation of rust, it is necessary to eliminate various corrosive factors before plating or other rust prevention measures. In this study, we investigated improvement of the corrosion resistance of steel surfaces by mechanochemical-multifunction cavitation (MC-MFC) with a sodium hypochlorite solution and MFC in water.

Free Research Field

表面改質

Academic Significance and Societal Importance of the Research Achievements

本研究では水中で錆が発生しない鋼材表面を作製するため，機能性キャビテーション(MFC)技術に次亜塩素酸ナトリウム液を加え，耐食性の改善について検討した．MFC処理した表面は大気中に発生するさびの抑制に有効的であるが，長期間を考慮すると赤錆の発生を完全には予防することが困難である．しかし，メッキ処理前の防処理前の処理として，MFC処理は不純物の除去または表面の化合物の形成によりメッキ処理よる保護被膜の密着強度の向上に寄与する可能性を示唆した．