Increment of the strength and ductility of high-strength multi-phase steel by optimizing the characteristics of ferrite

2023 Fiscal Year Final Research Report

• Project/Area Number: 21K14423
• Research Category: Grant-in-Aid for Early-Career Scientists
• Allocation Type: Multi-year Fund
• Review Section: Basic Section 26040:Structural materials and functional materials-related
• Research Institution: Aichi Institute of Technology (2023); Nagoya University (2021-2022)
• Principal Investigator: Ogawa Toshio 愛知工業大学, 工学部, 准教授 (10708910)
• Project Period (FY): 2021-04-01 – 2024-03-31
• Keywords: 鉄鋼材料 / 複相組織 / 強度-延性バランス / 再結晶 / 相変態 / 析出 / フェライト

Outline of Final Research Achievements

We attempted to dramatically improve the strength-ductility balance of high-strength multi-phase steel by optimizing the characteristics of ferrite. The obtained results revealed that the strength-ductility balance of dual phase steel with microstructure is composed of ferrite and martensite can be dramatically improved by making the ferrite equiaxed, refined, and hardened. We also focused on the three-dimensional morphology of ferrite, and the relationship between quantitative information on dislocation substructures and ferrite recrystallization behavior, and clarified the dominant factors that determine the characteristics of ferrite.

Free Research Field

構造用金属材料

Academic Significance and Societal Importance of the Research Achievements

本研究で対象としている複相組織鋼は、自動車用鉄鋼材料として広く用いられている。年々自動車用鉄鋼材料に対する高強度化のニーズが高まる中で、本研究では複相組織鋼のフェライトの特徴を最適化することで、飛躍的な強度-延性バランスの向上に成功した。したがって、本研究で開発した複相組織鋼は、次世代の自動車用鉄鋼材料としての実用化が期待される。また、フェライトの三次元形態、さらには転位組織の定量情報とフェライト再結晶挙動の関係にも着目し、フェライトの特徴を決定づける支配因子についても明らかにした点は、学術的にも極めて重要な意義を持つ。