2022 Fiscal Year Final Research Report
Adhesion Durability of Next-Generation Adhesion Systems Based on New Modality Evaluation
Project/Area Number |
21K16977
|
Research Category |
Grant-in-Aid for Early-Career Scientists
|
Allocation Type | Multi-year Fund |
Review Section |
Basic Section 57030:Conservative dentistry-related
|
Research Institution | Nihon University |
Principal Investigator |
SAI Keiichi 日本大学, 歯学部, 専修医 (80843151)
|
Project Period (FY) |
2021-04-01 – 2023-03-31
|
Keywords | 歯質接着性 / ユニバーサルアドヒーシブ応用型プライマー / 2ステップ接着システム / 初期接着性 / ヌープ硬さ |
Outline of Final Research Achievements |
A new two-step adhesive using universal adhesive technology, G2-Bond Universal, was tested. Two conventional two-step adhesives, Clearfil SE Bond 2 and OptiBond eXTRa, and an established universal adhesive, Scotchbond Universal Plus Adhesive, were used as comparison materials. Twelve specimens per group were used to measure the shear bond strength (SBS) to bovine enamel in different etching modes. The bonded specimens were stored in distilled water at 37°C for 5 min or 1, 6, 12, or 24 h before SBS testing. The KHN of the adhesive layer and resin composite was determined after the same storage periods as for SBS testing. All adhesives exhibited increased SBS with prolonged storage periods, irrespective of the etching mode. The KHN of the adhesive layer and resin composite increased over time.
|
Free Research Field |
歯科保存学
|
Academic Significance and Societal Importance of the Research Achievements |
近年,ユニバーサルアドヒーシブをプライマーとして用いる2ステップ接着システムが臨床応用された。この接着システムは,機能性モノマーを含むHEMAフリーのプライマーと高い疎水性を有するアドヒーシブから構成され,従来の2ステップセルフエッチングシステムと同等以上の接着耐久性を有することが報告されている。一方,光重合型コンポジットレジン修復においては,コンポジットレジン充填時の光照射直後から,様々な負荷が接着界面に加わっている。歯質接着性を臨床的な観点から評価するため,充填直後の接着強さおよびKHNの推移について検討することで,その接着メカニズムについて新たな知見を得ることができた。
|