Pore size and affinity controle of zeolite by the decpration of ZIF fragments

2023 Fiscal Year Final Research Report

• Project/Area Number: 21K18836
• Research Category: Grant-in-Aid for Challenging Research (Exploratory)
• Allocation Type: Multi-year Fund
• Review Section: Medium-sized Section 26:Materials engineering and related fields
• Research Institution: Kansai University
• Principal Investigator: Araki Sadao 関西大学, 環境都市工学部, 准教授 (00599152)
• Co-Investigator(Kenkyū-buntansha): 山本 秀樹 関西大学, 環境都市工学部, 教授 (30174808) ; 廣田 雄一朗 名古屋工業大学, 工学(系)研究科(研究院), 准教授 (60632437) ; 長谷川 泰久 国立研究開発法人産業技術総合研究所, 材料・化学領域, 研究グループ長 (90392646)
• Project Period (FY): 2021-07-09 – 2024-03-31
• Keywords: ゼオライト / 分離膜 / イミダゾール / ZIF / フラグメント修飾

Outline of Final Research Achievements

In this study, as new strategy for the control of the effective zeolite pore size, introducing a zeolites imidazolate framework (ZIF) fragment onto the walls of zeolite pores. ZIF fragment decoration was carried out by cation-exchanged FAU type, MOR type, and MFI type zeolite membranes with cobalt ions or zinc ions, respectively, and react with 2-methylimidazole(mIM). Co-FAU membrane modified with mIM showed the decrease of SF6 permeance and the increase of ideal separation factor for H2/SF6 and N2/SF6, significantly, which suggest that the ZIF fragment decoration is effective as a pore size control method of zeolite membranes.

Free Research Field

膜分離工学

Academic Significance and Societal Importance of the Research Achievements

FAU型、MOR型、MFI型ゼオライト膜をコバルトイオンまたは亜鉛イオンでそれぞれ交換し、2-メチルイミダゾールで処理することでZIFフラグメント修飾を行った。中でも、Coイオン交換FAU膜をZIFフラグメント修飾した膜はSF6の透過係数が大きく減少することを見出し、ZIFフラグメント修飾がゼオライト膜の細孔径制御技術として有効である可能性を示したことは学術的意義が高いと考えられる。今後も様々なイオン種による交換やイミダゾール種の違いにより精緻な細孔径制御技術として発展することが期待される。