2013 Fiscal Year Final Research Report
Establishment of the New Forming Guideline for Colloidal Nanoparticles
| Project/Area Number |
22360275
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Kagoshima University |
|---|
Principal Investigator |
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
SAMESHIMA Soichiro 鹿児島大学, 理工学研究科, 准教授 (00274861)
MATSUNAGA Naoki 宮崎大学, 工学部, 准教授 (40405543)
|
|---|
| Project Period (FY) |
2010-04-01 – 2014-03-31
|
| Keywords | ナノ粒子 / 加圧ろ過 / コロイドサスペンション / レオロジー / 動的粘弾性 / 成形体密度 / 圧縮強度 / ガス透過性 |
|---|
| Research Abstract |
A new forming guideline for colloidal nanoparticles was established based on the following experimental results: (1-1) The Effect of an Amino Acid of Low Molecular Weight on Consolidation of Nanoparticle Suspensions, (1-2) Influence of Pressure and Suspension Temperature on Filtration of Aqueous Alumina Suspensions, (1-3) Pressure Filtration of Alumina Suspensions under Alternating Current Field, (2-1) Temperature Dependence of Complex Modulus of Alumina Suspensions and Alumina Powder Compacts, (2-2) Influence of Phenylalanine on Viscoelastic Properties of Alumina Suspensions, (3-1) Rheology and Pressure Filtration of Aqueous SiC Suspensions of Nanometer-sized Bimodal Particles, (3-2) Compressive Mechanical Properties of Porous Alumina Powder Compacts, (3-3) Analysis of Gas Permeability of Porous Alumina Powder Compacts, (3-4) Microstructural Control and Gas Permeability of Porous Silicon Carbide.
|