2023 Fiscal Year Final Research Report

Study on technology to suppress the elution of hexavalent chromium in recycled aggregate concrete using ground granulated blast furnace slag

Research Project

  • PDF
Project/Area Number 22K20469
Research Category

Grant-in-Aid for Research Activity Start-up

Allocation TypeMulti-year Fund
Review Section 0304:Architecture, building engineering, and related fields
Research InstitutionOyama National College of Technology

Principal Investigator

Fumino Hikaru  小山工業高等専門学校, 建築学科, 助教 (80966929)

Project Period (FY) 2022-08-31 – 2024-03-31
Keywords再生骨材 / 六価クロム / 高炉スラグ微粉末
Outline of Final Research Achievements

The purpose of this study was to develop a technology to inhibit the elution of hexavalent chromium in recycled aggregate concrete using ground granulated blast-furnace slag.
The amount of hexavalent chromium eluted from concrete samples before carbonation using any recycled aggregate was less than the soil environmental standard of 0.05 mg/L. It was suggested that the leaching of hexavalent chromium from carbonated recycled aggregate concrete was suppressed by replacing a part of the cement with at least 25% ground granulated blast-furnace slag.

Free Research Field

建築材料

Academic Significance and Societal Importance of the Research Achievements

近年、資源の不足により世界中でリサイクル材の利用が進められており、コンクリートの分野においても解体コンクリート片を使用した再生骨材の利用が進められている。そこで本研究では再生骨材を利用する上で懸念される六価クロム溶出について検討を行った。
本研究の成果より、再生骨材を用いたコンクリートの六価クロム溶出に対して高炉スラグ微粉末を用いることで抑制することが明らかとなった。この結果より再生骨材を利用する際の環境的配慮の面で有効であることを示していると考られる。