2013 Fiscal Year Final Research Report
Development of automotive high-strength materials without using rare earth
| Project/Area Number |
23560890
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Metal making engineering
|
|---|
| Research Institution | Iwate University |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2011 – 2013
|
| Keywords | 球状黒鉛鋳鉄 / 高強度化 / 黒鉛粒数 / レアアースレス / アルカリ土類金属 |
|---|
| Research Abstract |
In the sample treated with a spheroidizer containing 0.01% La and 0.025% Ca, the graphite nodule count became 916 number/mm2,which is much higher than the graphite nodule count, 836 number/mm2, of the sample treated with the commercial spheroidizer(RE0.045%).Good mechanical properties, the tensile strength of 460MPa and elongation of 25%, were obtained in 30mm daiameter specimen.By the amount of RE was able to be reduced to about 1/4 compared with the RE content of a commercial spheroidizer using the spheroidizer with La and Ca.
|