2012 Fiscal Year Final Research Report
Development of Self-crack-healing Coating Technique and its Application for Heat Resistant Superalloy
| Project/Area Number |
23656091
|
|---|
| Research Category |
Grant-in-Aid for Challenging Exploratory Research
|
| Allocation Type | Multi-year Fund |
|---|
| Research Field |
Materials/Mechanics of materials
|
|---|
| Research Institution | University of Hyogo |
|---|
Principal Investigator |
UCHIDA Hitoshi 兵庫県立大学, 大学院・工学研究科, 教授 (30047633)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
NAKATANI Masanori 兵庫県立大学, 大学院・工学研究科, 助教 (80581553)
HANAKI Satoshi 兵庫県立大学, 大学院・工学研究科, 准教授 (20336829)
|
|---|
| Research Collaborator |
NISHIMURA Junki 兵庫県立大学, 大学院・工学研究科, 大学院生
|
|---|
| Project Period (FY) |
2011 – 2012
|
| Keywords | 自己き裂治癒 / セラミックスコーティング / 薄膜 / 高温 / 酸化 |
|---|
| Research Abstract |
A SiNx/SiCy nano-laminated film with a self-crack-healing ability under high temperature environment was fabricated. The influence of healing condition and film structure on the healing ability was investigated. In the case of the SiN monolayer film, the crack was poorly healed after heating. On the other hand, in the SiNx/SiCy nano-laminated film, crack healing occurred. The crack healing improved on increasing the heating temperature and time. There is a trade-off between the self-crack-healing ability and the thermal shock resistance in SiNx/SiCy nano-laminated film.
|
Research Products
(5 results)