2013 Fiscal Year Final Research Report
Primary recrystallization of covalent single-crystal semiconducting materials
Project/Area Number |
23686106
|
Research Category |
Grant-in-Aid for Young Scientists (A)
|
Allocation Type | Single-year Grants |
Research Field |
Material processing/treatments
|
Research Institution | Kyoto University |
Principal Investigator |
MORISHITA Kohei 京都大学, エネルギー科学研究科, 特定助教 (00511875)
|
Project Period (FY) |
2011-11-18 – 2014-03-31
|
Keywords | 半導体結晶 / 高温塑性変形 / 一次再結晶 / シリコン |
Research Abstract |
Single crystal semiconducting materials like silicon, which is brittle in nature owing to its covalent character, easily crack at a small load. Therefore, almost researchers "believe" it is impossible to deform them largely. As the results, primary recrystallization of silicon has not been studied although primary recrystallization by heat-treatment after large deformation is common knowledge in metal materials field. In the present study, large deformation of single-crystal silicon bulk at the temperature just below the silicon melting point was demonstrated, and the primary recrystallization of them were studied.
|