2012 Fiscal Year Final Research Report
Establishment of tool wear suppressing method for ceramic tool in cutting of free-machining steel for high speed machining
| Project/Area Number |
23760111
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Multi-year Fund |
|---|
| Research Field |
Production engineering/Processing studies
|
|---|
| Research Institution | Hiroshima University (2012)
Kanazawa University (2011) |
|---|
Principal Investigator |
TANAKA Ryutaro 広島大学, 大学院・工学研究院, 准教授 (60361979)
|
|---|
| Project Period (FY) |
2011 – 2012
|
| Keywords | セラミック工具 / 機械構造用炭素鋼 / BN快削鋼 / 旋削加工 / 正面フライス切削工具摩耗 / べラーグ / 切削温度 |
|---|
| Research Abstract |
The tool lives in turning of BN free-machining steel were obvious longer than those of standard steel. In particular, the tool life of TiC added alumina ceramic tool reached about 10 hours in the case that the tool life criteria was set at VB=0.3mm. This tool life was twice as long as that of coated carbide tool. In intermittent cutting, when depth of cut was set at relatively small, TiC added alumina ceramic tool was able to be used.
|