2014 Fiscal Year Final Research Report
Effects of a grain orientation of mixed conductive ceramics on oxygen pemeation properties
Project/Area Number |
23760637
|
Research Category |
Grant-in-Aid for Young Scientists (B)
|
Allocation Type | Multi-year Fund |
Research Field |
Inorganic materials/Physical properties
|
Research Institution | Nagoya Institute of Technology |
Principal Investigator |
KAGOMIYA Isao 名古屋工業大学, 工学(系)研究科(研究院), 准教授 (40318811)
|
Project Period (FY) |
2011-04-28 – 2015-03-31
|
Keywords | 混合導電性酸化物 / 酸素透過性 / イオン導電率 / 結晶構造 |
Outline of Final Research Achievements |
We investigated crytal structure and oxygen vacancy formation of SrFeO3-d using single crystal/powder neutron diffraction and X-ray diffraction method. It was found that the crystal symmetry of the SrFeO3-d was monoclinic, which was different from the reported one. With increasing tempeartature, oxygen vacancies were preferably created at the specific O sites. We prepared a SrFeO3-d ceramics, whose grains were mostly oriented along c-axis. The oxygen permeation flux of the grain oriented sample was higher than that of the non-oriented sample.
|
Free Research Field |
無機物性
|