2014 Fiscal Year Final Research Report
The relationships between precipitation of B2 phase and unique hardening behavior in Au-Ag-Pd-Cu alloy
| Project/Area Number |
24592973
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Dental engineering/Regenerative dentistry
|
|---|
| Research Institution | Aichi Gakuin University |
|---|
Principal Investigator |
FUKUI Hisao 愛知学院大学, 歯学部, 教授 (50090147)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
TSURUTA Syouzo 愛知学院大学, 歯学部, 准教授 (40183488)
|
|---|
| Project Period (FY) |
2012-04-01 – 2015-03-31
|
| Keywords | 歯科用金銀パラジウム合金 / 高温容体化処理 / B２型規則相 / Ｌ１０型規則相 |
|---|
| Outline of Final Research Achievements |
The purpose of this study was to clarify the mechanism of the unique hardening of dental Au-Ag-Pd-Cu alloy by high-temperature Solid solution treatment(ST).The relationships between precipitation of β′ phase and unique hardening behavior in Au-Ag-Pd-Cu alloy were also investigated.The results are as follows. It was clarified that the precipitation of the β' phase by high-temperature ST for 3.6ks strongly conttributes to the unique hardening behavior. The formation mechanism of β′ phase was elucidate and it is expected that the mechanical strength of dental Au-Ag-Pd-Cu alloy can be enhanced by controlling the microstructure of the β′ phase.
|
| Free Research Field |
歯科理工学
|