2013 Fiscal Year Final Research Report
Thermally stimulated infrared spectroscopy and its application to molecular structure analysis of carrier traps in organic semiconductor thin films
| Project/Area Number |
24655177
|
|---|
| Research Category |
Grant-in-Aid for Challenging Exploratory Research
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Functional materials/Devices
|
|---|
| Research Institution | Waseda University |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2012-04-01 – 2014-03-31
|
| Keywords | 赤外分光 / 有機半導体 / トラップ / P3HT / PCBM / 有機薄膜太陽電池 |
|---|
| Research Abstract |
We have studied infrared spectral changes of PEDOT:PSS/P3HT:PCBM films, which are active materials of organic thin film solar cells, upon irradiation of 532 nm light. Spectral changes were observed upon 60 min irradiation. The observed spectra are likely attributed to the overlaps of the bands due to trapped positive polarons in P3HT and chemical species generated by light irradiation. They are stable at room temperature. Large spectral changes were observed with increasing temperature, which are attributed to the changes of spectrum of PEDOT:PSS. Thus, it is difficult to obtain the activation energy of the trapped polarons. We will obtain the activation energy by measuring the rate of the reactions at several temperatures.
|