2013 Fiscal Year Final Research Report
Development of the divalent cation conducting solid electrolytes
| Project/Area Number |
24750202
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Multi-year Fund |
|---|
| Research Field |
Inorganic industrial materials
|
|---|
| Research Institution | Osaka University |
|---|
Principal Investigator |
TAMURA Shinji 大阪大学, 工学(系)研究科(研究院), 講師 (80379122)
|
|---|
| Project Period (FY) |
2012-04-01 – 2014-03-31
|
| Keywords | イオン伝導体 / 固体電解質 / 2価イオン / マグネシウム / ストロンチウム |
|---|
| Research Abstract |
In this study, we aimed to develop the novel divalent cation conducting solid electrolytes with three dimensional network structure, and we have demonstrated that the NASICON type (MgxHf1-x)4/(4-2x)Nb(PO4)3 and (Sr0.05Hf0.95)4/3.9(Nb1-yWy)5/(5+y)(PO4)3 solids showed the Mg2+ and Sr2+ cation conduction. Furthermore, the (Mg0.1Hf0.9)4/3.8Nb(PO4)3 solid was revealed to have the highest Mg2+ conductivity below 400 oC.
|