2013 Fiscal Year Final Research Report
Preparation of Oxide Mesocrystal Films and Their Application to Transparent Conducting Films
| Project/Area Number |
24860031
|
|---|
| Research Category |
Grant-in-Aid for Research Activity Start-up
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Shinshu University |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2012-08-31 – 2014-03-31
|
| Keywords | 酸化亜鉛 / 水溶液法 / 透明導電膜 / スピンスプレー法 |
|---|
| Research Abstract |
In this research, we aim low-temperature fabrication of metal oxide crystal films for substitution of tin-doped indium oxide by a new film processing technique which can achieve low environmental load, high deposition rate, and cost effectiveness. ZnO films with visible-light transparency over 70 percents and electrical resistivity about 5X10-3 ohm cm were successfully fabricated by spin-spray method with controlling the flow rate of solution and rotation rate of table. When water-soluble polymer was used as an additive, the crystal shape was changed by different manner with trisodium citrate. The performance of ZnO films prepared by using water-soluble polymer was not improved compared with those prepared with trisodium citrate. The results indicated that the adsorbed organics and film structure strongly affected electrical properties.
|