2015 Fiscal Year Final Research Report
Fabrication of Solar Cell by Metal Oxide Thin-film through molecular precursor method
Project/Area Number |
25410204
|
Research Category |
Grant-in-Aid for Scientific Research (C)
|
Allocation Type | Multi-year Fund |
Section | 一般 |
Research Field |
Energy-related chemistry
|
Research Institution | Kogakuin University |
Principal Investigator |
SATO MITSUNOBU 工学院大学, 公私立大学の部局等, 教授 (10154105)
|
Project Period (FY) |
2013-04-01 – 2016-03-31
|
Keywords | 分子プレカーサー法 / 薄膜 / 金属酸化物太陽電池 |
Outline of Final Research Achievements |
We examined the possibility to fabricate the translucent and dry-type solar cells by the molecular precursor method which is one of the wet processes for thin film formation of metal oxides. The translucent and dry-type solar cells by combination with a p-type Cu2O thin film were fabricated on AZO pre-coated substrate by the wet process. The structure of the solar cell was AZO/n-TiO2/ p-Cu2O. When the visible-light responsive titania was fabricated between the AZO and Cu2O, the solar cell provided the power conversion efficiency (η) of 0.001 %. Thus, it was elucidated that the present molecular precursor method has a possibility to be useful for the facile fabrication of the Vis-responsive dry solar-cell on large-area substrates.
|