2015 Fiscal Year Final Research Report
Fabrication of Transparent Nanohybrids with Heat Resistance Using High-Density Amorphous Formation and Uniform Dispersion of Nanodiamond
| Project/Area Number |
25410219
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Polymer/Textile materials
|
|---|
| Research Institution | Saitama University |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2013-04-01 – 2016-03-31
|
| Keywords | 機能性ナノフィラー / 結晶性透明高分子材料 / 表面改質 / ナノ分散 / 耐熱性透明フィルム |
|---|
| Outline of Final Research Achievements |
A new technology for the production of transparent material using a “crystalline” polymer is proposed in the present study. Further, transparent and flexible crystalline polymer nanohybrid film containing well-dispersed nanodiamond filler was fabricated. Partially fluorinated crystalline polymer with switchboard-type lamellae results in high transparency as a consequence of the formation of a high-density amorphous structure based on high-temperature drawing just below the melting point at 110 °C. Although the formation of nanohybrid materials composed of fluorinated-polymer/organo-modified nanocarbon is generally difficult, we confirmed the formation, via melt-compounding, using atomic force microscopy and wide-angle X-ray diffraction. Even though the polymer matrix/nanodiamond hybrid has remarkable aggregation properties, a well-dispersed state was achieved because of improvement in wettability obtained through surface modification of filler.
|