2015 Fiscal Year Final Research Report
Glass formation based on the chalcohalide systems and properties and structure of the glasses
Project/Area Number |
25410239
|
Research Category |
Grant-in-Aid for Scientific Research (C)
|
Allocation Type | Multi-year Fund |
Section | 一般 |
Research Field |
Inorganic industrial materials
|
Research Institution | Kyoto Institute of Technology |
Principal Investigator |
KADONO KOHEI 京都工芸繊維大学, 材料化学系, 教授 (00356792)
|
Co-Investigator(Kenkyū-buntansha) |
WAKASUGI TAKASHI 京都工芸繊維大学, 材料化学系, 教授 (40222400)
|
Project Period (FY) |
2013-04-01 – 2016-03-31
|
Keywords | ガラス / 非酸化物ガラス / カルコハライドガラス / 硫化物ガラス / ガラス形成 / 赤外透過材料 / 分相 / ガラス転移温度 |
Outline of Final Research Achievements |
Glass formation was examined for the sulfide and halide-mixed systems, in which the sulfides are GeS2, Ga2S3, Sb2S3, and the halides are CsX or AgX (X=Cl, Br, I). The properties, such as glass transition temperature, refractive index, and optical properties, and their dependences on halide content were systematically investigated. The CsX of 20 - 30 mol% were incorporated for the GeS2-Sb2S3-CsX systems. It was suggested that phase separation occurs in the GeS2-Sb2S3-AgCl and Ga2S3-Sb2S3-CsCl systems. The absorption edge in the infrared region for the Ga2S3-Sb2S3-CsX glasses shifted to 1 to 2 um compared with those of the conventional sulfide glasses. This indicated that the glass system has a potential applicability for infrared materials.
|