2015 Fiscal Year Final Research Report
Improvement of precision and efficiency in the zone refining method for the ultra-high-purity aluminum of a purity of 7N level
| Project/Area Number |
25420794
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Metal making/Resorce production engineering
|
|---|
| Research Institution | Hiroshima Kokusai Gakuin University |
|---|
Principal Investigator |
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
WATANABE Mahiko 広島国際学院大学, 工学部, 教授 (70341188)
NAKAMURA Masayoshi 広島国際学院大学, 工学部, 准教授 (80412295)
|
|---|
| Project Period (FY) |
2013-04-01 – 2016-03-31
|
| Keywords | 帯溶融精製 / 超高純度 / アルミニウム / 残留抵抗比 / GDMS分析 |
|---|
| Outline of Final Research Achievements |
In order to develop a technology for purifying aluminum materials stably at a purity of 7N level, we carried out the experiments of zone melting purification, the evaluation of purified specimens and the simulation of the purification process. Also we discussed purification mechanism of zone melting refining method. By simulation, with a melting width of 200mm it is estimated to be able to efficiently purify in the purification of about 5 path. On the other hand, by the temperature measurement, it was confirmed that the maximum temperature rises as the melting width becomes long. Accordingly, by a melting width of about 150 mm, it became clear that zone melting purification is achieved to a purity of 7N level from 5N level aluminum with a small number of passes of about 5.
|
| Free Research Field |
材料工学
|