2015 Fiscal Year Final Research Report
Development of process of synthesis of micron polymeric particle and its applications
| Project/Area Number |
25420817
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Reaction engineering/Process system
|
|---|
| Research Institution | Nagoya University (2014-2015)
Hiroshima University (2013) |
|---|
Principal Investigator |
Yamamoto Tetsuya 名古屋大学, 工学(系)研究科(研究院), 准教授 (10432684)
|
|---|
| Project Period (FY) |
2013-04-01 – 2016-03-31
|
| Keywords | ソープフリー乳化重合 / ミクロン粒子 / 共重合 / 両親媒性モノマー / 油溶性開始剤 / 高濃度化 / 炭素繊維強化プラスチック / 界面接着性 |
|---|
| Outline of Final Research Achievements |
This study investigated the development of micron-sized polymeric particle by soap-free emulsion polymerization using oil-soluble initiator, and its application. As a result, the particle size was varied from 300 nm to 20 μm changing the ionic strength by electrolyte for short reaction time. Amphipathic monomer, N-vinylacetamide, was used for the copolymerization to enhance the particle concentration. These techniques was applied to synthesize carbon fiber reinforced plastic (CFRP). The carbon fibers was coated with polymeric particles to improve the surface adhesion between the carbon fiber and the resin. This method was useful to enhance the performance of CFRP.
|