2014 Fiscal Year Final Research Report
Analysis of heat denaturation layer of an Er:YAG laser irradiated-dentin and development of new adhesive for lased-dentin
Project/Area Number |
25861815
|
Research Category |
Grant-in-Aid for Young Scientists (B)
|
Allocation Type | Multi-year Fund |
Research Field |
Conservative dentistry
|
Research Institution | The Nippon Dental University |
Principal Investigator |
KATO Chikage 日本歯科大学, 新潟生命歯学部, 助教 (00459926)
|
Project Period (FY) |
2013-04-01 – 2015-03-31
|
Keywords | 象牙質 / Er:YAG laser / 接着 / コンポジットレジン |
Outline of Final Research Achievements |
Following experimental conditions, cavity preparation and surface conditioning of the cavity, were conducted using Er:YAG laser; ExpG1: #120~#600 waterproof abrasive paper (Control), ExpG2: 50mJ/10pps irradiation, ExpG3: 150mJ/10pps irradiation, ExpG4: 250mj/10pps irradiation, ExpG5: 50mJ/10pps →150mJ/10pps irradiation, ExpG6: 150mJ/10pps irradiation→ H3PO4(30sec), ExpG7:150mJ/10pps irradiation→ H3PO4(30sec)→ NaClO(90sec), ExpG8: 150mJ/10pps irradiation→ H3PO4(30sec)→ silane coupling treatment, ExpG9: 150mJ/10pps→ 50mJ/10pps irradiation. Azan Stains were employed heat denaturation layers colored in red were observed in the laser irradiation groups. Little changes were observed on SEM but large changes were observed on specimens in laser irradiation groups of TEM. The collagen fibers structure changes were led by the above mentioned same factors. On EPMA observation, concentration declines of both Ca, P, and Mg were observed some groups.
|