2018 Fiscal Year Final Research Report
Development of the novel thermodynamics integrating a solid and its aqueous ion and the stringent safety measure for crisis of accumulation of the nuclear fuel wastes
| Project/Area Number |
26420758
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Metal making/Resorce production engineering
|
|---|
| Research Institution | University of Hyogo |
|---|
Principal Investigator |
|
|---|
| Research Collaborator |
Gamjäger Heinz Univ. Montan, Prof.
Perrone Jane Headquarters in Paris, NEA, OECD
|
|---|
| Project Period (FY) |
2014-04-01 – 2019-03-31
|
| Keywords | 環境浄化 / 低負荷 / 環境調和 / 熱力学サイクル / 地球環境 / 放射性物質 / 相安定性 / 飽和溶解度 |
|---|
| Outline of Final Research Achievements |
To determine the thermodynamic values for aqueous ions, the experiment including many different methods should be done. The third law entropies for the solids, for instance, should be measured to determine the standard entropies of formation of aqueous ions satisfying the thermodynamic cycles to perfection. The thermodynamic measurements for clarifying the whole picture of the thermodynamic values from the solids to aqueous ions were done.
The thermodynamic values for the yellow phases formed in the nuclear fuel wastes as well as their molybdic aqueous ion were determined. The standard Gibbs energies of solution for the molybdic actinide complex oxides, which were hardly measured, were predicted on the basis of the present determined values.
|
| Free Research Field |
金属・資源生産工学
|
| Academic Significance and Societal Importance of the Research Achievements |
原子力発電による使用済核燃料は廃棄できないまま、世界中に蓄積されている。この使用済核燃料を化学処理によってガラス固化体に成型、鉄鋼とコンクリ－トの人工バリアに装填後、地層処分する政策がある。 しかしながら、千年を超えた後、あるいは、大地震などによって人工バリアが崩壊すると，ガラス固化体が地下水に接触する危険性がある。
ガラス固化体中に生成するイエロ－フェ－ズ結晶群の固相とイオンの熱力学諸量を決定し、これらが水溶液に溶出する溶解度平衡定数を決定した。また、結果に基づき、アクチノイドモリブデン酸化物の溶解度定数を予測した。本成果はOECDパリ本部地球化学電算機データバンクに登録される。
|