Development of high-strength fabrication method of porous particulates by gelation of organic slurry and control method of porous structure

Research Project

  • PDF
Project/Area Number 26630389
Research Category

Grant-in-Aid for Challenging Exploratory Research

Allocation TypeMulti-year Fund
Research Field Properties in chemical engineering process/Transfer operation/Unit operation
Research InstitutionKyoto University

Principal Investigator

TAMON Hajime  京都大学, 工学(系)研究科(研究院), 教授 (30111933)

Project Period (FY) 2014-04-01 – 2016-03-31
Keywordsゾル‐ゲル法 / 微粒子成形 / 一方向凍結 / テンプレート合成 / 構造制御
Outline of Final Research Achievements

Activated carbon powders, zeolite powders and carbon nanohorns were added to organic gels synthesized from phenol and formaldehyde, and carbon cryogels containing particulates were prepared by unidirectional freezing, freeze drying and pyrolysis. The particulates were fabricated to honeycomb morphology, and porous properties of carbon cryogels were improved by mixing activated carbons or zeolites.
Next, alumina particulates were molded by unidirectional freezing of slurry including gelatin as a binder, and then alumina sintered bodies were obtained. High-strength alumina sintered bodies with honeycomb morphology and uniform pore distribution were successfully prepared by tuning preparation conditions. Platinum supported alumina sintered bodies could be also prepared without special reduction treatments.