1988 Fiscal Year Final Research Report Summary
Studies on Prepavation and Properties of Film Caleium Puosphate Materials
| Project/Area Number |
62470067
|
|---|
| Research Category |
Grant-in-Aid for General Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
無機工業化学
|
|---|
| Research Institution | Tokyo Metropolitan University |
|---|
Principal Investigator |
UMEGAKI Takao Faculty of Technology, 工学部, 助教授 (70087287)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
CHIKAZAWA Masatoshi Faculty of Technology, 工学部, 教授 (90087289)
INOUE Hiroyuki Faculty of Technology, 工学部, 助手 (10193608)
YAMASHITA Kimihiro Faculty of Technology, 工学部, 助手 (70174670)
|
|---|
| Project Period (FY) |
1987 – 1988
|
| Keywords | 電気泳動 / スパッタリング / 水酸アパタイト / リン酸カルシウムガラス / アルコール / アミド / チタン板 |
|---|
| Research Abstract |
Phosphate film of coating for ceramics and metals by electrophoresis and sputtering was studied by means of ESCA, IR and X-ray diffraction. On the electrophretic formation of hydroxyapatite film on Ti plate the mixture of alcohols and amides and the mixture of a alcohols and dimethlsuphoxide were found to be most appropriate dispersion medium. The amounts of films on Ti plate in those mixtures increased remarkably compared with those in the respective pure solvents. Amorphous calcium orthophosphate on Ti plate was obtained by sputtering, using calcium phosphate glass (CaO/P_2 O_5= 55/45) as a target. A small amount of condensed phosphates in films was detected by IR. Chain phosphates were partially decomposed during the sputtering. The phosphate content in the sputtered films was smaller than that of the target glass.
|
Research Products
(13 results)