Diveropment of alpha-TCP/DCPD Bioactive Bone Cement
| Project/Area Number |
02670666
|
|---|
| Research Category |
Grant-in-Aid for General Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Orthopaedic surgery
|
|---|
| Research Institution | Kitasato University, School of Medicine |
|---|
Principal Investigator |
MORITA Masafumi Kitasato Univ. Sch. of Med. Dept. Biomed. Eng., Asis. Prof., 医学部, 講師 (20112667)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
ITOMAN Moritoshi Kitasato Univ. Sch. of Med. Dept. Orthop., Asoc. Prof., 医学部, 助教授 (70104528)
|
|---|
| Project Period (FY) |
1990 – 1991
|
| Project Status |
Completed (Fiscal Year 1991)
|
| Budget Amount *help |
¥1,900,000 (Direct Cost: ¥1,900,000)
Fiscal Year 1991: ¥700,000 (Direct Cost: ¥700,000)
Fiscal Year 1990: ¥1,200,000 (Direct Cost: ¥1,200,000)
|
|---|
| Keywords | Bioactive Bone Cement / alpha-TCP / Joint Prosthesis / Biocompatibility / 複合材料 / 骨親和性 |
|---|
| Research Abstract |
1. The ratio of compositions alpha -TCP/DCPD and the strength
The maximum strength of bone cement was obtained at the alpha -TCP added 10% DCPD and the ratio of bone cement powder and solution. Three days after mixing. the maximum strength of 57MPa was appeared and the cement was weekend gradually.
2. The Viscosity of cement paste
This cement will be used for the perpase of fixation of artificial joint or filling material of bone defect. Due to these uses, the cement should liave suitable viscosity for easy treatment. The viscosity : will be governed with the contents of powder and liquid. Then we are ovser ved that 10% of DCPD added cement mixed with two times much of liquid was most suitable.
3. Biocompatibility test for the bone cement
Intramedulary canal of femur of living rabbit was drilled from the distal end to 2 cm length proximal direction. And then the cement paste Was injected through the canal. After 0.5 and I years, we preparated some bone tissue samples. of the rabbits and observed the histrogy. But, no information was observed at the interface of bone tissue.
|