ARBにより作製されたナノ組織Ni合金の組織、集合組織と機械的性質

Research Project

Project/Area Number07F07409
Research Category

Grant-in-Aid for JSPS Fellows

Allocation TypeSingle-year Grants
Section外国
Research Field Material processing/treatments
Research InstitutionKyoto University(2008-2009)
Osaka University(2007)
Host Researcher 辻 伸泰  
Foreign Research Fellow BHATTACHARJEE P  
BHATTACHARJEE Pinaki Prasad  京都大学, 大学院・工学研究科, 外国人特別研究員
BHATTACHARJEE P. P.  
BHATTACHARJEE Pinaki Pras  大阪大学, 大学院・工学研究科, 外国人特別研究員
Project Period (FY) 2007
Project Status Completed(Fiscal Year 2009)
Budget Amount *help
¥2,300,000 (Direct Cost : ¥2,300,000)
Fiscal Year 2009 : ¥500,000 (Direct Cost : ¥500,000)
Fiscal Year 2008 : ¥1,100,000 (Direct Cost : ¥1,100,000)
Fiscal Year 2007 : ¥700,000 (Direct Cost : ¥700,000)
Keywords巨大ひずみ加工 / ARB / Ni / 超微細粒 / 集合組織 / 剪断帯 / 変形双晶 / EBSD
Research Abstract

強圧延(圧下率95%)を施したNi-5at%W合金における圧延集合組織および再結晶集合組織の発達を基礎的に調べた。冷間圧延材は、全体としては典型的な純金属型あるいはCu型の集合組織を示したが、局所的に勇断を受けた領域とその他のマトリクスの間には、ミクロ組織およびミクロ集合組織に大きな差異があることが見出された。一次再結晶集合組織は、Cube方位({100}<001>)およびRotated-Cube方位({013}<100>)およびそれらの双晶方位から構成されていた。変形ままの組織中に、CubeおよびRotated-Cube方位を有する微細なバンド状組織の存在が確認された。Cube方位粒は、局所的に剪断を受けた領域からは離れた領域で核生成した。一方、非Cube方位の再結晶粒は、局所剪断領域およびその周辺で生成した。こうした観察結果より、強圧延されたNi-5wt%W合金におけるCube集合組織の発達は、加工組織中のCubeバンドからの優先核生成により説明できると考えられる。
また、研究室内での他研究員との共同研究により、HPT(high pressure torsion)を利用した巨大ひずみ加工に伴う集合組織の発達の影響を、高純度アルミニウムを用いて明らかにした。その結果、一方向加工と双方向加工の間で、形成される集合組織に大きな差異があることを初めて明らかにした。

Report

(2results)
  • 2008 Annual Research Report
  • 2007 Annual Research Report

Research Products

(6results)

All 2009 2008

All Journal Article Presentation

  • [Journal Article] Cold Rolling and Recrystallization Textures of a Ni-5at%W Alloy2009

    • Author(s)
      P. P. Bhattacharjee, R. K. Ray, N. Tsuji
    • Journal Title

      Acta Mater. (印刷中)

    • Related Report
      2008 Annual Research Report
    • Peer Reviewed
  • [Journal Article] Texture Evolution in Pure Aluminum Subjected to Monotonic and Reversal Straining in High Pressure Torsion2009

    • Author(s)
      D. Orlov, P. P. Bhattacharjee, Y. Todaka, M. Umemoto, N. Tsuji
    • Journal Title

      Scripta Mater. (印刷中)

    • Related Report
      2008 Annual Research Report
    • Peer Reviewed
  • [Journal Article] Reversal Straining to Manage Structure in Pure Aluminum under SPD2008

    • Author(s)
      D. Orlov, P. P. Bhattacharjee, Y. Todaka, M. Umemoto, N. Tsuji
    • Journal Title

      Mater. Sci. Forum 584-586

      Pages : 133-138

    • Related Report
      2008 Annual Research Report
    • Peer Reviewed
  • [Journal Article] Microstructure and Texture Evolution during the Accumulative Roll Bonding of Pure Ni2008

    • Author(s)
      P.P. Bhattacharjee, D. Terada, and N. Tsuji
    • Journal Title

      Proc. Of MATS 2008 (in press)

    • Related Report
      2007 Annual Research Report
    • Peer Reviewed
  • [Presentation] On the evolution of {001}<100> texture in a heavily cold rolled and recrystallized Ni-5at. %W alloy2009

    • Author(s)
      Pinaki P. Bhattacharjee
    • Organizer
      日本金属学会秋季大会
    • Place of Presentation
      熊本大学
    • Year and Date
      2009-09-25
    • Related Report
      2008 Annual Research Report
  • [Presentation] Microstructure and Texture Evolution during the Accumulative Roll Bonding of Pure Ni2008

    • Author(s)
      P.P. Bhattacharjee, D. Terada, and N. Tsuji
    • Organizer
      International Conference on Microstructure and Texture in Steels
    • Place of Presentation
      Jamshedpur, India
    • Year and Date
      2008-02-06
    • Related Report
      2007 Annual Research Report

URL :

Published : 2007-04-01   Modified : 2016-04-21  

Information FAQ News Terms of Use

Powered by NII kakenhi