Grant-in-Aid for International Scientific Research.
|Section||Joint Research .|
|Research Institution||Nara National Cultural Properties Research Institute|
SAWADA Masaaki Nara National Cultural Properties Director of Research Research Institute, Center for Division Archaeological Operations, 埋蔵文化財センター・研究指導部, 研究指導部長 (20000490)
CORT L.T. Smithonian Institution, Freer Curator Gallery of Art, Arthur M.Sackler Gallery,, フリヤー・サックラー美術館, 学芸研究員
ZELST L.V. スミソニアン研究機構, 保存分析研究所, 所長
平尾 良光 東京国立文化財研究所, 保存科学部, 室長 (40082812)
三浦 定俊 東京国立文化財研究所, 保存科学部, 部長 (50099925)
斉藤 孝正 文化庁, 文化財保護部・美術工芸課, 文化財監査官
三輪 嘉六 文化庁, 文化財保護部, 文化財監査官
TATSUMI Junichiro Nara National Cultural Properties Head of Research Lab. Research Insititute, Div, 飛鳥藤原宮跡発掘調査部, 室長 (10110090)
NISHIMURA Yasushi Nara National Cultural Properties Head of Research Lab. Research Insititute, Cen, 埋蔵文化財センター・研究指導部, 室長 (80000488)
CORT L.T スミソニアン研究機構, フリアー・サックラー美術館, 室長
ZELST L.V スミソニアン研究機構, 保存分析研究所, 所長
三輸 嘉六 文化庁, 文化財保護部, 文化財監査官
CON L.T. スミソニアン研究機構, フリマー・サックラー美術館, 学芸研究員
MACHIDA Akira Agency for Cultural Affairs, 文化財保護部, 監査官 (90000471)
|Project Fiscal Year
1996 – 1998
Completed(Fiscal Year 1998)
|Budget Amount *help
¥13,800,000 (Direct Cost : ¥13,800,000)
Fiscal Year 1998 : ¥5,000,000 (Direct Cost : ¥5,000,000)
Fiscal Year 1997 : ¥4,400,000 (Direct Cost : ¥4,400,000)
Fiscal Year 1996 : ¥4,400,000 (Direct Cost : ¥4,400,000)
|Keywords||ceramic / porcelain stone / chemical compositions of glaze / neutron activation anaysis / x-ray fluorescence analysis / old Kutani / Mino / Karatsu / 陶磁器 / 陶石 / 釉薬 / 放射化分析 / X線分析 / 古九谷 / 美濃 / 唐津|
1. Around 260 of ceramic sherds, excavled from kiln sites such as Mino, Seto, Kutani, Karatsu, and excavated from consumer sites were analyzed. As for data outside Japan, ceramic sherds in Vietnam, Thailand and Cambodia were collected and analyzed.
(1)Composition ratios of trace elements of bodies were determined by instrumental neutron activation analysis.
(2)Major elements such as Sr, Rb, and Zr were measured in micro-focus energy-dispersive X-ray fluorescenceanalysis. (3)Mineral compositions were examined in X-ray diffractometry. (4 )Chemical compositions of glaze and its colored materials were identified. (5)Lead isotope ratios of Chinese green-glazed ware belonging to Smithsonian Institutionwere measured.
2. Ceramic sherds excavated from Asazuma kiln (Kurume city, Fukuoka pref.), Yoshidaya, Miyamotoya, Kutani hon kilns (Yamashiro, Kaga city), Motoyashiki, Seianji, Jorinji nishido kilns No.2 and 3 (Toki city, Gifu pref.) were analyzed. Although kilns in Yamashiro remained the same loc
ation, three groups of skilled workers alternately managed the manufacturing industry. The distinction of the groups was clarified by comparing the composition ratios of Rb and Sr. The chemical composition of glaze depends on the kilns in which ceramics were burnt. It was clarified that the body was used in a clear distinction between earthenware and porcelain in Yamashiro kilns. Analyzing cobalt-blue glaze used for ash-glazed ware excavated from many kilns in Mino and Yamashiro, the amounts of Mn as a colored material differ from those of each other kiln. As for Khumer earthenware in Angkor period in Cambodia, Kiln sites in Run Ta Ek Tani was surveyed and the micro samples chipped off the surface of the sherds were analyzed. At the same time, the sherds owned by Smithsonian Institution were measured and examined to compare with the data from Run Ta EK Tani.
3. On March 8, 1999, International Research Conference was held at Smithsonian Institution as a fruit of chemical analysis on the ceramics. Less