| Project/Area Number |
08F08614
|
|---|
| Research Category |
Grant-in-Aid for JSPS Fellows
|
| Allocation Type | Single-year Grants |
|---|
| Section | 外国 |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | National Institute for Materials Science |
|---|
Principal Investigator |
任 暁兵 独立行政法人物質・材料研究機構, センサ材料センター, グループリーダー
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
WANG Yu (独)物質・材料研究機構, センサ材料センター, 外国人特別研究員
|
|---|
| Project Period (FY) |
2008 – 2010
|
| Project Status |
Completed (Fiscal Year 2010)
|
| Budget Amount *help |
¥2,300,000 (Direct Cost: ¥2,300,000)
Fiscal Year 2010: ¥500,000 (Direct Cost: ¥500,000)
Fiscal Year 2009: ¥800,000 (Direct Cost: ¥800,000)
Fiscal Year 2008: ¥1,000,000 (Direct Cost: ¥1,000,000)
|
|---|
| Keywords | strain glass / shows shape memory effect / superelasticity / Landau-Ginzburg model / damping / kinetics / relaxation spectrum |
|---|
| Research Abstract |
最近、strain glassは重要な新しいが概念として注目され、科学的に重要な意味を持っている。(本研究では、上記の研究から得られた新しい知見に基づいて、強磁性体のcluster spin glass、誘電体のrelaxor及び強弾性体のstrain glassにおける新規物性を探ることを目的とする。更に、これらの新規物性を利用して、新機能材料及び新アクチュエータなどの創出の可能性も提案する。
今年度では、高いガラス変態温度を持つGum合金におけるstrain glassの存在する可能性及びGum合金の特異な挙動の起源について研究し、Ti-Ni二元系及びTi-Ni-X三元系においてStrain glassの共通特徴を探索した。具体的に以下の成果が得られた。
1.Ti-Nb及びGum Metalはstrain glass合金であることをDMAお呼びTEM実験で証明した。Gum合金の特異な挙動はStrain glassに関係していることが分かった。
2.Ti-Ni及びTi-Ni-X合金系のStrain glass状態図が驚異的な類似性を発見した。つまり、添加元素濃度或いは点欠陥濃度がある臨界濃度を超えると、マルテンサイト変態が消失し、strain glassが現れる。Landau-Ginzburgモデル及びPhase fieldシミュレーションでstrain glass転移の再現に成功した。
|