Research of "vacancy epitaxy"
| Project/Area Number |
12650006
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Applied materials science/Crystal engineering
|
|---|
| Research Institution | The University of Tokyo |
|---|
Principal Investigator |
UENO Keiji The University of Tokyo, Graduate School of Science, 大学院・理学系研究科, 助手 (40223482)
|
|---|
| Project Period (FY) |
2000 – 2001
|
| Project Status |
Completed (Fiscal Year 2001)
|
| Budget Amount *help |
¥3,600,000 (Direct Cost: ¥3,600,000)
Fiscal Year 2001: ¥1,100,000 (Direct Cost: ¥1,100,000)
Fiscal Year 2000: ¥2,500,000 (Direct Cost: ¥2,500,000)
|
|---|
| Keywords | 空孔 / 空孔規則配列 / Ga_2Se_3 / エピタキシャル成長 / C_<60> / bilayer-GaSe終端Si(111) / 多孔性物質 / フォトルミネッセンス / Ga2Se3 / C60 |
|---|
| Research Abstract |
(1) I tried to grow Ga vacancy-ordered Ga_2Se_3 epitaxial films on Si (100) substrates. In order to obtain a single-domain epitaxial film I used a vicinal Si (001) substrare, whose clean surface has the 2×1 single-domain reconstruction. In addition, the lattice constant of the Si is almost same with that of Ga_2Se_3. It has been found that Ga vacancy-ordered single-domain Ga_2Se_3 films can be grown on the vicinal Si (001) substrates with the growth condisions ; substrate temperature = 480℃, VI/III ratio > 100. At the substrate temperature higher than 500℃, no Ga vacancy ordering was observed. At lower substrate temperature than 420 ℃, polycrystalline growth occurred. At the VI/III ratio of 10, no Ga vacancy-ordering was found, too. Photoluminescence spectra taken at 6.5K showed very btoad luminescence peak around 650 〜 1000 nm. No polarized photoluminescence was observed from the Ga vacancy-ordered Ga2Se3 film, which suggests that the grown film on the vicinal Si (001) substrate has the monoclinic crystal structure.
|