| Co-Investigator(Kenkyū-buntansha) |
IWAI Kazuhiko Nagoya University, Engineering, Professor, 大学院・工学研究科, 助教授 (80252261)
SUN Mun Gyu Nagoya University, Engineering, Research Assistant, 大学院・工学研究科, 助手 (00397481)
佐々 健介 名古屋大学, 大学院・工学研究科, 助教授 (30101166)
|
|---|
| Budget Amount *help |
¥122,330,000 (Direct Cost: ¥94,100,000、Indirect Cost: ¥28,230,000)
Fiscal Year 2005: ¥4,940,000 (Direct Cost: ¥3,800,000、Indirect Cost: ¥1,140,000)
Fiscal Year 2004: ¥17,290,000 (Direct Cost: ¥13,300,000、Indirect Cost: ¥3,990,000)
Fiscal Year 2003: ¥45,760,000 (Direct Cost: ¥35,200,000、Indirect Cost: ¥10,560,000)
Fiscal Year 2002: ¥44,460,000 (Direct Cost: ¥34,200,000、Indirect Cost: ¥10,260,000)
Fiscal Year 2001: ¥9,880,000 (Direct Cost: ¥7,600,000、Indirect Cost: ¥2,280,000)
|
|---|
| Research Abstract |
I.Research on carbon materials :
The following knowledge has been found. (1)The heat treatment of carbon fibers under a high magnetic field of 5T and weak tension strengthens double the mechanical strength of carbon fibers. (2)Mesophase microspheres with homogenous size can be formed by heating a tar pitch under a high magnetic field. (3)The reaction in which mesophase particles are formed by decomposing mesitylene under high pressure, is considerably disturbed by imposition of a magnetic field of 10T.
II.Research on biomaterials :
The uni-directional crystal alignment of biomaterials such as hydroxyapatite (HAp) is useful for bone reparation. (1)A novel process where a sample is rotated during a slip casting under a high magnetic field has newly been proposed to fabricate uni-directionally oriented compacts. This new process indicated that crystal orientation as high as about 100% was obtained. (3)Moreover, the fabrication of HAp/collagen composite also was carried out. Highly oriented c
… More
ollagen fibers and weakly crystallized HAp crystals were fablicated.
III.Research on nonmagnetic metals :
It has been found that the imposition of a high magnetic field during solidification can align Zinc crystal orientation.
IV.Research on ceramics :
Uni-directionally oriented compacts of structural Si_3N_4 ceramics and thermoelectric Bi_2Te_3 ceramics were fabricated by rotating a sample during slip casting under a high magnetic field. This method was developed to prepare the compact with multilayer of uni-directionally oriented compact of Si_3N_4, which had higher mechanical strength than that without crystal orientation. The figure of merit for fabricated Bi_2Te_3 1.3 at 323K, is the highest value among the values reported hitherto.
V.Research on development of an in situ, method to quantify a phase transformation rate :
A new method to quantify a phase transformation rate has developed and applied to γ/α phase transformation. This method is in situ and enables to clearly determine the start and end points of the transformation. Less
|