Project/Area Number |
14571871
|
Research Category |
Grant-in-Aid for Scientific Research (C)
|
Allocation Type | Single-year Grants |
Section | 一般 |
Research Field |
補綴理工系歯学
|
Research Institution | Matsumoto Dental University |
Principal Investigator |
KUROIWA Akihiro Matsumoto Dental University, Department of dentistry, Professor, 歯学部, 教授 (10195571)
|
Co-Investigator(Kenkyū-buntansha) |
UDA Go Matsumoto Dental University, Department of dentistry, Assistant, 歯学部, 助手 (30350838)
|
Project Period (FY) |
2002 – 2003
|
Project Status |
Completed (Fiscal Year 2003)
|
Budget Amount *help |
¥3,500,000 (Direct Cost: ¥3,500,000)
Fiscal Year 2003: ¥1,500,000 (Direct Cost: ¥1,500,000)
Fiscal Year 2002: ¥2,000,000 (Direct Cost: ¥2,000,000)
|
Keywords | Gypsum Bonded Investment / Recycling / Mechanical Property / 歯科用石膏系埋没材 |
Research Abstract |
Measurement of expansion at the time of hardening. Control showed 0.44(±0.01) % and with 10% addition was 0.46(±0.01) %,20%addition 0.34(±0.02)%, 30%addition 0.30(±0.022)%, 40%addition 0.18(±0.022)%, and 50%addition 0.12(±0.03)%. The tendency for a value to decrease was shown as the value increased at the time of 10% addition and the amount of addition increased from 20%. Measurement of heating expansion Control showed 1.074%. The amount of expansion became 1.129% by addition of 100/., 0.972% by addition of 200%., 1.048% by addition of 30%., 1.102% by addition of 40%., 1.194% by addition of 50%. Measurement of compression strength Before calcination, the tendency for a value to decrease was shown as the value increased at the time of 10% addition and the amount of addition increased from 20%. After calcination, the tendency for a value to decrease was shown as the value increased at the time of 10% addition and the amount of addition increased from 20%. Fitness examination The tendency which a value increases was shown as the value decreased at the time of 10% addition and the amount of addition increased from 20%. Measurement of surface coarseness The tendency which a value increases was shown as the value decreased at the time of 10% addition and the amount of addition increased from 20%. Surface coarseness of Investment Before calcination, the tendency which a value increases was shown as the value decreased at the time of 20% addition and the amount of addition increased from 30%. After calcination, the tendency which a value increases was shown as the value decreased at the time of 10% addition and the amount of addition increased from 20%. Measurement of hardening time Hardening time showed a tendency to decrease as the amount of addition increased.
|