低温トポタクティック反応による新規機能性遷移金属酸化物の合成と構造物性評価
| Project/Area Number |
15F15036
|
|---|
| Research Category |
Grant-in-Aid for JSPS Fellows
|
| Allocation Type | Single-year Grants |
|---|
| Section | 外国 |
|---|
| Research Field |
Inorganic chemistry
|
|---|
| Research Institution | Kyoto University |
|---|
Principal Investigator |
島川 祐一 京都大学, 化学研究所, 教授 (20372550)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
DENIS ROMERO FABIO 京都大学, 化学研究所, 外国人特別研究員
|
|---|
| Project Period (FY) |
2015-10-09 – 2017-03-31
|
| Project Status |
Completed (Fiscal Year 2016)
|
| Budget Amount *help |
¥2,300,000 (Direct Cost: ¥2,300,000)
Fiscal Year 2016: ¥1,100,000 (Direct Cost: ¥1,100,000)
Fiscal Year 2015: ¥1,200,000 (Direct Cost: ¥1,200,000)
|
|---|
| Keywords | 機能性酸化物 / 低温トポタクティック反応 / 遷移金属酸化物 |
|---|
| Outline of Annual Research Achievements |
昨年度より発展的にペロブスカイト構造化合物を中心に研究を展開してきた。特に異常高原子価Feイオンを含む酸化物で、逐次的に電荷不均化と電荷移動という2つの転移が起こる新物質の合成に成功し、特に電荷不均化した状態において、アイドルスピンを有する極めて特異な磁気構造が現れることを見出した。一連の発見は、Feの異常高原子価電子状態の不安定性が新たな形で解消されるとともに、電荷転移が特異な磁気構造を安定化させていることを明らかにした点でも重要である。
This year's work has focused on the synthesis and characterization of cation ordered and/or charge transition oxides using high pressure and low temperature, topochemical methods. Notable results include the elucidation of unusual charge behavior in Ca0.5Bi0.5FeO3 displaying charge disproportionation and intermetallic charge transfer transitions, results which have been published in Angewandte Chemie International Edition and in a forthcoming publication submitted to Physical Review Letters.
On the unusual charge behavior in Ca0.5Bi0.5FeO3, A-site cation substitution leads to small changes in the structure but large effects on the resulting material properties (eg Sr0.5Bi0.5FeO3 does not show charge ordering or charge transfer). A-site substitution of RE cations for Ca in CaFeO3 allows for an investigation of the role of structure on the charge disproportionation behavior. A large amount of data was collected during a recent neutron diffraction experiment and analysis is ongoing.
|
| Research Progress Status |
28年度が最終年度であるため、記入しない。
|
| Strategy for Future Research Activity |
28年度が最終年度であるため、記入しない。
|
Report
(2 results)
Research Products
(9 results)