Effects of pre-drying and coexisting materials on expansion of cement hadrened body due to secondary ettringite formation
| Project/Area Number |
16K06438
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Civil engineering materials/Construction/Construction management
|
|---|
| Research Institution | Niigata University |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2016-04-01 – 2019-03-31
|
| Project Status |
Completed (Fiscal Year 2018)
|
| Budget Amount *help |
¥4,810,000 (Direct Cost: ¥3,700,000、Indirect Cost: ¥1,110,000)
Fiscal Year 2018: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000)
Fiscal Year 2017: ¥650,000 (Direct Cost: ¥500,000、Indirect Cost: ¥150,000)
Fiscal Year 2016: ¥3,380,000 (Direct Cost: ¥2,600,000、Indirect Cost: ¥780,000)
|
|---|
| Keywords | 硫酸塩劣化 / エトリンガイト / 二次生成 / モノサルフェート / C-S-H / C-A-S-H / 27Al NMR / Al配位数 / モノカーボネート / Siのbridging site / 遅れエトリンガイト生成 / 共存物質 / 前処理乾燥 / XRD/Rietveld解析 / 遅延エトリンガイト / 乾燥・温度条件 / 結合水 / 水蒸気吸着 / FT-IR |
|---|
| Outline of Final Research Achievements |
The present study experimentally examined the effects of monosulfate pre-drying conditions and coexisting materials on secondary ettringite formation. Synthesized monosulfate samples dried under varying conditions and with coexisting materials such as C-S-H were mixed with a sodium sulfate solution, and the amount of secondary ettringite was found to increase following drying under 0% or 11% relative humidity. The secondary ettringite proportion was also markedly increased by the presence of C-S-H, regardless of the pre-drying conditions, and calcium-aluminate-silicate-hydrates (C-A-S-H) containing four-coordinate Al were formed in these samples. It is evident that ettringite is likely to form from four-coordinate Al, and that C-S-H promotes secondary ettringite formation because it transitions six-coordinate Al derived from the monosulfate to four-coordinate Al by substituting Al in the Si chains.
|
| Academic Significance and Societal Importance of the Research Achievements |
遅延EttやC-S-Hに含まれる水の存在形態およびその構成比について着目し，未だ実証されていないFamyらによる「仮説」を，単純化した「実験」によって，共存物質であるC-S-Hの影響を「定量的」に「把握・実証」しようとする試みは世界初であり，また乾燥条件の制御やC-S-Hの影響を「定量的」に把握するために, 水蒸気吸着等温線の測定，コンダクションカロリメータによる測定および27Al-NMRによるEttの形状・構造解析等，これまで用いられてこなかった新しい分析技術を用いて「実証する」ことは学術的かつ独創的な点であると考えられる．
|