Low-temperature synthesis of oxynitrides for development of new functional materials
| Project/Area Number |
17H04950
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (A)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | Hokkaido University |
|---|
Principal Investigator |
MIURA Akira 北海道大学, 工学研究院, 准教授 (10603201)
|
|---|
| Project Period (FY) |
2017-04-01 – 2020-03-31
|
| Project Status |
Completed (Fiscal Year 2019)
|
| Budget Amount *help |
¥24,310,000 (Direct Cost: ¥18,700,000、Indirect Cost: ¥5,610,000)
Fiscal Year 2019: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
Fiscal Year 2018: ¥6,630,000 (Direct Cost: ¥5,100,000、Indirect Cost: ¥1,530,000)
Fiscal Year 2017: ¥15,730,000 (Direct Cost: ¥12,100,000、Indirect Cost: ¥3,630,000)
|
|---|
| Keywords | 酸窒化物 / 窒化物 / 酸素還元触媒 / 半導体 / メタセシス反応 / 低温合成 / 電気化学触媒 / 電子構造 / 機能性 / 低温反応 |
|---|
| Outline of Final Research Achievements |
This reserch project aims to propose the new synthesis method for oxynitrides without long heat treatment, and to emerge new functional materials. Our achievement includes the combustion reaction from chloride, oxyhydride and amide to form BaNbO2N and BaTaO2N. Mn incorporation into Mo2N framework changed its electronic structure and improved the catalytic activity toward oxygen reduction reaction.
|
| Academic Significance and Societal Importance of the Research Achievements |
本研究では、新規機能性材料を生み出すための新たな合成手法の創出と、酸化物イオンと窒化物イオンを組み合わせた新規材料の創出を目指して研究を行った。その結果、ナトリウムアミドと塩化物、酸水化物の混合によって、光触媒として着目されている酸窒化物ペロブスカイト型を数秒で合成することに成功した。また、新規窒化物であるマンガン―モリブデン窒化物を発見し、マンガンが窒化物格子中にはいることで、電子構造が変化し酸素還元触媒能が向上した。さらに、液相を介した半導体薄膜の機能性向上を目指し、酸化インジウム薄膜の電子移動度の向上に成功した。
|