Development of technology for formation and its control of nanostructures on solid surfaces with ultrashort pulse lasers
| Project/Area Number |
18206010
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (A)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Applied optics/Quantum optical engineering
|
|---|
| Research Institution | Kyoto University |
|---|
Principal Investigator |
MIYAZAKI Kenzo Kyoto University, エネルギー理工学研究所, 教授 (50293957)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
YASUMARU Naoki , 福井工業高等専門学校機械工学科, 教授 (90158006)
MIYAJI Godai , 京都大学エネルギー理工学研究所, 助教 (30378905)
|
|---|
| Project Period (FY) |
2006 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥49,010,000 (Direct Cost: ¥37,700,000、Indirect Cost: ¥11,310,000)
Fiscal Year 2008: ¥5,330,000 (Direct Cost: ¥4,100,000、Indirect Cost: ¥1,230,000)
Fiscal Year 2007: ¥13,130,000 (Direct Cost: ¥10,100,000、Indirect Cost: ¥3,030,000)
Fiscal Year 2006: ¥30,550,000 (Direct Cost: ¥23,500,000、Indirect Cost: ¥7,050,000)
|
|---|
| Keywords | 光プロセッシング / フェムト秒レーザー / ナノ周期構造 / アブレーション / 近接場 / 表面プラズモン・ポラリトン / ナノテクノロジー / ナノ構造生成・制御 / DLC / 硬質薄膜 / プラズモン・ポラリトン / ナノ構造生成 / 選択的結合構造転移 / 局所場 / メゾスコピック域 |
|---|
| Research Abstract |
フェムト秒レーザーパルスによるナノ周期構造生成・制御に関する研究を行い, 世界に先駆けてその物理過程を解明することに成功した。アブレーションによるナノ周期構造の生成を担っている主要な物理過程が, 表面の微小凹凸面での「局所場(近接場)」の発生, 及び凹凸面を介して入射光電場でと表面を結合する「表面プラズモン・ポラリトン」による周期増強電場の発生であることを突き止めた。この物理モデルは, 誘電体, 半導体, 及び金属に対しても適用できることを確認した。
|