Anisotropic thick film magnets prepared by high-speed PLD method and their application to an advanced and small motor
| Project/Area Number |
19360147
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Electronic materials/Electric materials
|
|---|
| Research Institution | Nagasaki University |
|---|
Principal Investigator |
NAKANO Masaki Nagasaki University, 工学部, 准教授 (20274623)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
福永 博俊 長崎大学, 工学部, 教授 (10136533)
|
|---|
| Project Period (FY) |
2007 – 2009
|
| Project Status |
Completed (Fiscal Year 2009)
|
| Budget Amount *help |
¥18,980,000 (Direct Cost: ¥14,600,000、Indirect Cost: ¥4,380,000)
Fiscal Year 2009: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2008: ¥3,770,000 (Direct Cost: ¥2,900,000、Indirect Cost: ¥870,000)
Fiscal Year 2007: ¥13,910,000 (Direct Cost: ¥10,700,000、Indirect Cost: ¥3,210,000)
|
|---|
| Keywords | 電気 / 電子材料 / 磁性 / PLD法 / 厚膜磁石 / 高速成膜 / エネルギー積 / マイクロモータ / ドロップレット / YAGレーザ / 異方性磁石膜 / 保磁力 / 添加物 / 小型モータ / 高成膜速度 / 基板加熱 / 異方性 / ミリサイズモータ |
|---|
| Research Abstract |
In the study, an improvement in magnetic properties of anisotropic and isotropic Nd-Fe-B film magnets was carried out by using additives. In addition, several applications comprising the films were investigated. The obtained results are as followed.
(1) Anisotropic Nd-Fe-B films
An obtained film prepared from the Nd_<2.4>Fe_<14>B+Ga_<0.5at.%> target had the coercivity, remanence and (BH)_<max> values of approximately 850 kA/m, 0.95 T and 150 kJ/m^3, respectively. These magnetic properties are superior compared with those for the anisotropic PLD-made Nd-Fe-B films without additives. We also confirmed that the intensities of a X-ray diffraction peaks corresponding to the c-planes such as (004), (006) and (008) of the film were stronger than those of the additive-free film.
(2) Isotropic film magnets
PLD-made isotroipic Nd-Fe-B thick film magnets were prepared from targets with Zr, Nb and Ga, respectively. They were crystallized by two annealing methods of conventional annealing (CA) and pulse annealing (PA), respectively. In the case of using Nd_<2.6>Fe_<14>B targets, 0.5 at.% Zr, Nb and Ga addition increased the coercivity of the film by approximately 100～300 kA/m compared with that of additive-free samples prepared by CA method. We also confirmed further increase in coercivity of the film by PA method and the obtained film prepared from a Nd_<2.6>Fe_<14>B+Ga_<0.5at.%> target had large coercivity of approximately 1700 kA/m.
(3) Applications
We applied the above-mentioned films to a friction-drive motor and a milli-size motor.
|