Improvement of the oxidation resistance of the alloys considering the effective use of the resources
| Project/Area Number |
19560722
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Material processing/treatments
|
|---|
| Research Institution | Yokohama National University |
|---|
Principal Investigator |
YOSHIHARA Michiko Yokohama National University, 大学院・工学研究院, 特別研究教員 (70111705)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000)
Fiscal Year 2008: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000)
Fiscal Year 2007: ¥3,770,000 (Direct Cost: ¥2,900,000、Indirect Cost: ¥870,000)
|
|---|
| Keywords | チタンアルミ合金 / 軽量耐熱材料 / 高温酸化 / 酸化皮膜はく離 / 活性元素添加 / Nb / 表面処理 / アルミ拡散浸透処理 / 拡散浸透処理 / Nb添加量 / 耐酸化性改善 / 酸化皮膜 / はく離挙動 / アコースティックエミッション |
|---|
| Research Abstract |
軽量耐熱材料であるTiAl基合金の耐酸化性改善を目的として研究を行なった. TiAl基合金は高温からの冷却中に酸化皮膜がはく離しやすい. その抑制には活性元素であるY添加は有効であるが, Zr添加ははく離を促進する可能性がある. また, TiAlの耐酸化性はNb添加量に依存して改善されるが, 低Nb合金に簡便な表面処理法であるAl拡散浸透処理を適用すると, 長時間にわたって高Nb合金よりもさらに良好な耐酸化性を維持できることが明らかとなった.
|
Report