A study on the growth and dissolution of crystals in a peritectic system
| Project/Area Number |
19560750
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Metal making engineering
|
|---|
| Research Institution | National Institute for Materials Science |
|---|
Principal Investigator |
MAIWA Koji National Institute for Materials Science, 情報通信材料研究萌芽ラボ, 主任研究員 (10343849)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
木村 秀夫 独立行政法人物質・材料研究機構, 情報通信材料研究萌芽ラボ, グループリーダー (50343843)
|
|---|
| Project Period (FY) |
2007 – 2010
|
| Project Status |
Completed (Fiscal Year 2010)
|
| Budget Amount *help |
¥4,680,000 (Direct Cost: ¥3,600,000、Indirect Cost: ¥1,080,000)
Fiscal Year 2010: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2009: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2008: ¥910,000 (Direct Cost: ¥700,000、Indirect Cost: ¥210,000)
Fiscal Year 2007: ¥1,950,000 (Direct Cost: ¥1,500,000、Indirect Cost: ¥450,000)
|
|---|
| Keywords | 包晶 / 核形成 / 結晶成長 / 準安定 / 安定相 / 準安定相 |
|---|
| Research Abstract |
We aimed to elucidate the favorable conditions and mechanisms to peritectic microstructure on the basis of the in situ observations of the solidification processes in Sr(NO3)2-H2O system. Although α and β phases are stable at above and below peritectic temperature, respectively, α phase nucleated initially at any temperature and β phase formed on the preexistent α phase. However, once β phase appeared, it grew much faster than α phase and envelop the α phase. These results show that contrary features in nucleation and growth of the two phases induce the peritectic microstructure.
|
Report
(6 results)
Research Products
(32 results)