Fatigue Strength and Tribological Properties of TiN Coated Steel Quenched after TiN Coating
| Project/Area Number |
19760073
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Materials/Mechanics of materials
|
|---|
| Research Institution | The University of Shiga Prefecture |
|---|
Principal Investigator |
TANABE Hirotaka The University of Shiga Prefecture, 工学部, 准教授 (00275174)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥2,850,000 (Direct Cost: ¥2,700,000、Indirect Cost: ¥150,000)
Fiscal Year 2008: ¥650,000 (Direct Cost: ¥500,000、Indirect Cost: ¥150,000)
Fiscal Year 2007: ¥2,200,000 (Direct Cost: ¥2,200,000)
|
|---|
| Keywords | 表面改質 / 薄膜 / 熱処理 / 破壊 / 疲労 / 摩耗 / 窒化チタン薄膜 / スパッタリング / 耐摩耗性 / 硬さ / 密着強度 |
|---|
| Research Abstract |
TiN被覆鋼の高機能化手法としての成膜後基板焼入れ処理の有効性や実用性を示すことを目的として,TiN被覆鋼の摩擦摩耗特性と転がり疲労強度に及ぼす成膜後基板焼入れ処理の影響を調べた.その結果,成膜後基板焼入れ処理により,TiN薄膜の耐摩耗性が大幅に改善されること,比較的低い応力レベルにおいて成膜後基板焼入れ処理による転がり疲労寿命の改善効果が得られる可能性のあることなどが明らかとなり,本処理の摺動部品や軸受への実用化の可能性が示された.
|