Effect of Absorbed Water Content of Adhered Mortar on Strength and Deformation Characteristics of Recycled Aggregate Concrete
| Project/Area Number |
19760305
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Civil engineering materials/Construction/Construction management
|
|---|
| Research Institution | Kyushu University |
|---|
Principal Investigator |
SAGAWA Yasutaka Kyushu University, 大学院・工学研究院, 助教 (10325508)
|
|---|
| Project Period (FY) |
2007 – 2008
|
| Project Status |
Completed (Fiscal Year 2008)
|
| Budget Amount *help |
¥3,600,000 (Direct Cost: ¥3,300,000、Indirect Cost: ¥300,000)
Fiscal Year 2008: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2007: ¥2,300,000 (Direct Cost: ¥2,300,000)
|
|---|
| Keywords | 再生骨材 / 再生骨材コンクリート / 吸水率 / 単位総水量 / 細孔容積 / 空隙 / 強度 / 空隙量 / 蛍光顕微鏡 |
|---|
| Research Abstract |
再生骨材を有効利用するためには,再生骨材の付着モルタルに捕捉される水分がコンクリートやモルタルの強度および耐久性に及ぼす影響について明らかにする必要がある。本研究では,水銀圧入式ポロシメータや蛍光顕微鏡の撮影画像から求めた空隙量と再生モルタルの強度との関係を求めた。その結果,再生骨材の吸水率が高いほど空隙量が多く,新セメントペースト部の粗大化により強度が低下することが明らかとなった。
|