| Research Abstract |
Martensitic transformation from ultrafine grained (UFG) austenite fabricated by accumulative roll bonding (ARB) process in a metastable austenitic alloy was studied. The martensite transformed from the UFG austenite showed characteristic morphology and texture. The martensite transformation starting (Ms) temperature increased after 1 cycle ARB, which was related to increasing amount of nucleation sites, such as low angle boundaries, introduced during early stage of ARB process. In contrast, by increasing the ARB cycles, Ms temperature decreased. The decrease in the Ms temperature could be correlated to strengthening of austenite by grain refinement.
|