| Project/Area Number |
20360338
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Material processing/treatments
|
|---|
| Research Institution | Kitakyushu National College of Technology |
|---|
Principal Investigator |
YAMADA Kenji Kitakyushu National College of Technology, 物質化学工学科, 特任教授 (80101179)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
MATSUSHIM Shigenori 北九州工業高等専門学校, 物質化学工学科, 教授 (80229476)
NAKAMURA Hiroyuki 北九州工業高等専門学校, 総合科学科, 教授 (70172434)
|
|---|
| Project Period (FY) |
2008 – 2010
|
| Project Status |
Completed (Fiscal Year 2010)
|
| Budget Amount *help |
¥11,180,000 (Direct Cost: ¥8,600,000、Indirect Cost: ¥2,580,000)
Fiscal Year 2010: ¥780,000 (Direct Cost: ¥600,000、Indirect Cost: ¥180,000)
Fiscal Year 2009: ¥4,550,000 (Direct Cost: ¥3,500,000、Indirect Cost: ¥1,050,000)
Fiscal Year 2008: ¥5,850,000 (Direct Cost: ¥4,500,000、Indirect Cost: ¥1,350,000)
|
|---|
| Keywords | 低温プラズマ / 光触媒 / 可視光 / ナノ構造 / ドーピング / 表面 |
|---|
| Research Abstract |
Highly visible-light-sensitive photocatalysts are developed with the formation of surface nanostructures controlled by plasma-surface interaction, as follows : (1) Nitrogen-doped surface layer are formed on surfaces of TiO_2 and transition metal-doped TiO_2, respectively. It becomes apparent that their band-gaps become narrow with the formation of the surface layer. (2) Cu-contained layer is formed on a surface of TiO_2 with plasma CVD using organometallic compound. Multi-electron-reactivity of the plasma CVD-treated TiO_2 can realize with the contained Cu reduced by visible-light-excited electrons. (3) Composite composed of Nb-doped TiO_2 as n-type semiconductor having nitrogen-doped surface layer and CuBi_2O_4 as p-type semiconductor shows Z-scheme mechanism in which visible-light-excited electron can be transferred form the n-type to the p-type semiconductor after each visible-light excitation in the semiconductors.
|