Inhibition of PGM Slag Loss in Copper smelting process
| Project/Area Number |
20560690
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Metal making engineering
|
|---|
| Research Institution | Iwate University |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2008 – 2010
|
| Project Status |
Completed (Fiscal Year 2010)
|
| Budget Amount *help |
¥4,940,000 (Direct Cost: ¥3,800,000、Indirect Cost: ¥1,140,000)
Fiscal Year 2010: ¥650,000 (Direct Cost: ¥500,000、Indirect Cost: ¥150,000)
Fiscal Year 2009: ¥1,300,000 (Direct Cost: ¥1,000,000、Indirect Cost: ¥300,000)
Fiscal Year 2008: ¥2,990,000 (Direct Cost: ¥2,300,000、Indirect Cost: ¥690,000)
|
|---|
| Keywords | 白金族金属 / 貴金属 / 分配係数 / スラグ / 溶銅 / 白金 / パラジウム / カルシウムフェライト / 分配比 / 銅製錬 / 溶解度 / 鉄シリケートスラグ / 酸素分圧 / ロジウム / ルテニウム / 金 / マット / 分配 |
|---|
| Research Abstract |
An experimental study was carried out to determine the distribution of precious metals (gold, platinum, palladium, rhodium, and ruthenium) between copper matte and FeO_x-SiO_2 slag phases and the solubility of platinum in FeO_x-SiO_2 slag. The distribution ratios of precious metals were measured at 1300℃ and a fixed partial pressure of SO_2 of 0.1 atm for the matte grades between 40 and 70 mass% of copper. It was found that the distribution ratios are around 10^<-2> for ruthenium, 10^<-3> for gold and platinum and palladium and 10^<-4> for rhodium. In addition, platinum solubility in the FeO_x-SiO_2 slag equilibrated with the Cu-Pt binary alloy has been investigated at 1300℃. The platinum solubility in the slag decreases with decreasing copper content in the slag. The reduction of the copper loss leads inhibition of the PGM loss in the slag.
|