Formation of nano-rod films of iron-group transition metals via wet plating in a strong magnetic field
| Project/Area Number |
20760505
|
|---|
| Research Category |
Grant-in-Aid for Young Scientists (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Metal making engineering
|
|---|
| Research Institution | Kyoto University |
|---|
Principal Investigator |
YAGI Shunsuke Kyoto University, 工学研究科, 助教 (60452273)
|
|---|
| Project Period (FY) |
2008 – 2009
|
| Project Status |
Completed (Fiscal Year 2009)
|
| Budget Amount *help |
¥4,420,000 (Direct Cost: ¥3,400,000、Indirect Cost: ¥1,020,000)
Fiscal Year 2009: ¥1,040,000 (Direct Cost: ¥800,000、Indirect Cost: ¥240,000)
Fiscal Year 2008: ¥3,380,000 (Direct Cost: ¥2,600,000、Indirect Cost: ¥780,000)
|
|---|
| Keywords | 組織制御 / 強磁性ナノ粒子 / 液相還元法 / 熱力学 / 混成電位 / サイクリックボルタンメトリー / 水晶振動子マイクロバランス |
|---|
| Research Abstract |
An electrochemical formation process of ferromagnetic iron-group metal or alloy nanoparticles was established through the present work. The shape of the iron-group metal or alloy nanoparticles was changed from sphere to rod or wire by conducting the synthesis process in a strong magnetic field. This process is expected as a novel shape-control method on a nanoscale.
|