| Outline of Final Research Achievements |
In-situ compression experiments of pillar-shaped sample were performed in a transmission electron microscope under controlled loads. The pillar-shaped sample preparation conditions by focused ion beam (FIB) were determined. In the experiment on a pillar-sample of Fe, a stress of about 14 GPa in the compressive direction was estimated, indicating a possible phase transition from alpha to epsilon phase. Morover, experiments on diamond pillar-shaped specimens showed that stresses in excess of 200 GPa were estimated to be applied in the compressive direction.
|